Compatible with most open-architecture 3D printers and 3D printing pens for broad usability
Available in 1.75 mm and 2.85 mm diameters to suit various printing needs
Prints similar to PLA with minimal warping for reliable results
Fully sinterable after printing, allowing parts to be fired in a furnace for complete metalization
Less hygroscopic than PLA, reducing risk of filament drying and degradation
Summarized by Shop
Create real metal parts using any open-architecture FFF/FDM 3D printer—or even a 3D printing pen. Available Formats: 1.75mm and 2.85mm diameters in 100g weight
Metal Load By Mass
Recommended Nozzle
Filament Density (g/cc)
Aluminum 6061
60.0 – 69.0%
0.6mm Hardened Steel, standard flow
1.20 – 1.50
Bronze
86.0 – 90.0%
0.6mm Hardened
Available Diameters
1.75 mm, 2.85 mm
Sample Weight
100 g
Material
Metal (various including aluminum, copper, iron, stainless steel, titanium, bronze, tungsten)
Recommended Nozzle Size
0.6 mm (for most tested printers)
Filament Density (g/cc)
Varies by material (e.g., aluminum 6061 60–69, copper 86–90, titanium 64–82)